4 Types of Metal 3D Printing Processes and Their Materials

Powder 3D printer systems are referred to as Powder Bed Fusion (PBF) or Powder Bed Additive Manufacture (PBAM). This 3D printing technique uses either an electron beam, laser, or heat to melt and fuse metal. Common metal 3D printer processes are SLS (Selective Laser Sintering), SLM (Selective Laser Melting), and DMP (Direct Metal Printing — or commonly known as DMLS (Direct Metal Laser Sintering)). PBF works by depositing powder onto the build table and spreading it across the platform using a roller or recoater blade. A laser is scanned over the build area and pulsed to melt the powder. The table descends by the layer thickness, and the process repeats until all layers are printed.

Table 1 below summarizes the pros and cons of metal powder bed fusion 3D printing.

DED (Directed Energy Deposition) is a metal 3D printing process that uses a focused energy source. This energy can either be a laser, a plasma arc, or an electron beam. DED uses powder and wire to create 3D printed parts. The DED powder and DED wire processes are quite different from PBF but similar to each other. With DED, deposition and fusion of metal occur at the same time. A nozzle deposits material into the energy source. The feedstock is melted and deposited as the X-Y traverse of the printhead progresses. When the layer is complete, the build table drops by the layer thickness resolution and the process repeats. When the build is complete, the part can be removed from the build table. Post-machining may be required for surface finish issues.

Table 2 below shows the pros and cons of DED.

The fusion filament processes of FDM (Fused Deposition Modeling) and FFF (Fused Filament Fabrication) in metal printing are in the early stages and have obstacles to overcome. Metal filament extrusion works by heating a filament made from both thermoplastic material and metallic particles. The filament is drawn through a nozzle and deposited on the build platform, layer-by-layer. The complete part is placed in a sintering furnace to burn out the plastic and sinter the metal. Metal filament extrusion is most useful for making metallic-looking parts that can be as accurate and detailed as plastic FDM.

Table 3 shows the pros and cons of metal filament extrusion.

Binder jetting is similar to the various PBF techniques, except that the particles are bonded with an adhesive that is deposited to build layers via an inkjet. Material jetting, on the other hand, is a distinct process that is similar in many regards to DED but is closest in nature to PolyJet. In binder jetting, the first powder layer is laid down; then, a printhead passes over the layer applying adhesive to bind the slice. The table drops by the z-build height, and the process repeats until the model is complete. Material jetting works with the layer inkjet printed in a powder-loaded UV-cured polymer matrix. This forms the layer and is cured in place by a UV light source. The table drops by the layer thickness, and the process are repeated until the “green” model is completed. Binder jetting and material jetting must account for the shrinkage on 3 axes when scaling the print. A precise result can be achieved, however, with good control of the sintering process. While the processes are different, there are several similarities in the pros and cons of binder jetting and material jetting. These similarities are shown in table 4 below.

Metal 3D printing is a laser-based technology that fuses metal particles layer-by-layer. This technology is commonly used for prototyping, production of parts with complex geometries, and end-use parts, as well as for the reduction of metal components in an assembly. Metal 3D printing is supplied with a growing family of materials. This satisfies the needs of diverse industries from jewelry to aerospace, and medical to plastics manufacturing. Some processes and equipment are material-specific and limited in their range, while others are capable of using a range of materials.

For more information, see our guide to 3d printing.

How Do I Select the Best Type of 3D Printing?

Selecting the best type of 3D printing is complex. Below are useful steps to go through when deciding which metal 3D printer processes to choose:

1. Review part requirements. For example, give consideration to the layer resolution, the need for the reproduction of fine detail, as well as the required mechanical properties and cosmetic quality considerations.
2. Choose a material family for the part. 
3. Once the material has been selected, review the available processes that use that material to consider the best one to produce the desired results.
4. Check the availability of resources, including suppliers for the material, time, and costs.

In choosing the best type of metal 3D printing, it is important to build experience—or access good advice from those already familiar with the various options.

What Are the Metal 3D Printing Materials?

There is a long and growing list of metal-type options in metal 3D printing materials. The most common metal types are:

1. Stainless Steel: Generally in 3 alloy groups: 304, 316, and 17-4. These are corrosion-resistant and of high strength when not porous.
2. Tool Steels D2, A2, and H13: Have high strength, are hardenable, wear-resistant, and are applicable for dies and tools.
3. Titanium and Ti64: Materials that are ideal for lightweight parts and have high strength.
4. Aluminum 7075, 4047, 6061, 2319, 4043: These are various lightweight alloys for general, lightweight components.
5. Inconel® 718, 625: These have low corrosion and high-temperature resistance for purposes such as engine parts.
6. Cobalt Chrome: Superalloy for biomedical and aerospace applications.
7. Gold/Silver: Pure metals for jewelry and limited biomedical uses.
8. Niobium, Niobium-Zirconium: These are high-temperature and high–chemical–resistance alloys for aerospace use.
9. Tantalum: Similar to Niobium but with better chemical resistance.
10. Hastelloy® Nickel Chromium: Materials that are tough—temperature-resistant and crack-resistant. Commonly used for turbine and nuclear components.
11. Tungsten and Alloys: Materials with super-high density. Used commonly for radiation shields, collimators, and engine parts.

When Did 3D Metal Printing First Appear?

The earliest practical execution of a metal 3D printer was the EOSINT M250. It was launched in 1994 by ElectroOptical Systems. It combined metal with a lower-temperature alloy, which was fused to couple the primary particles. In 2004, EOS launched the EOSINT M270. It was the first PBF system that used a diode pump 200W laser to melt the metal feedstock. Since then, there has been an exponential increase/improvement in methods, materials, and resolutions.

Is 3D Printed Metal Durable?

No. Not all 3D printed metals are durable. Metal 3D printer processes offer advantages but suffer disadvantages unique to their characteristics and material limitations. However, by selecting the right process and materials to suit the application, remarkable results can be achieved.

What Metal Powder Is Used for 3D Printing?

Metal powders come in a range of types, materials, and grades. These vary from the relatively coarse powders required for DMLS (and related technologies) down to the graded nanoparticles used in material jetting. The powders also range from spherical particles to rough shapes, depending on the nature of the process and the requirements in the end product.

How Is Metal Powder Used for 3D Printing?

A wide variety of metal powders are built up into finished components, using a range of application/fusion techniques and machines. The powder processes all work in the same way. Broadly speaking, the material is put into the build plate and fused to nearby particles, progressively building up a finished part.

This article reviewed four of the 3D printing technologies that are used for creating metal parts and products. To learn more about the types of 3D printing for metals and if it is the right technology for your application, contact a Xometry Representative.

Xometry provides a wide range of manufacturing capabilities, including 3D printing and value-added services for all of your prototyping and production needs. Visit our website to learn more or to request a free, no-obligation quote.

Copyright and Trademark Notices

1. Inconel® is a registered trademark of Huntington Alloys division of Special Metals Corp., Huntington, WV.
2. Hastelloy® s a registered trademark of Haynes International, Kokomo, Indiana.

Disclaimer

The content appearing on this webpage is for informational purposes only. Xometry makes no representation or warranty of any kind, be it expressed or implied, as to the accuracy, completeness, or validity of the information. Any performance parameters, geometric tolerances, specific design features, quality and types of materials, or processes should not be inferred to represent what will be delivered by third-party suppliers or manufacturers through Xometry’s network. Buyers seeking quotes for parts are responsible for defining the specific requirements for those parts. Please refer to our terms and conditions for more information.